|本期目录/Table of Contents|

[1]周爱军,付艳梅,彭旭,等.丙烯酸系四元共聚耐盐性高吸水树脂的合成[J].武汉工程大学学报,2012,(05):1-4.[doi::103969/jissn16742869201205001]
　ZHOU Ai\|jun,FU Yan\|mei,PENG Xu,et al.Synthesis of acryli quaternary salt\|tolerant superabsorbent resin[J].Journal of Wuhan Institute of Technology,2012,(05):1-4.[doi::103969/jissn16742869201205001]
点击复制

丙烯酸系四元共聚耐盐性高吸水树脂的合成(/HTML)
分享到：

《武汉工程大学学报》[ISSN:1674-2869/CN:42-1779/TQ]

卷:
期数:
2012年05期
页码:
1-4
栏目:
化学与化学工程
出版日期:
2012-05-31

文章信息/Info

Title:
Synthesis of acryli quaternary salt\|tolerant superabsorbent resin
文章编号:
16742869(2012)05000104
作者:
周爱军; 付艳梅; 彭旭; 万香港; 钟毅; 江学良
武汉工程大学材料科学与工程学院，湖北 武汉 430074
Author(s):
ZHOU Ai\|jun; FU Yan\|mei; PENG Xu;  WAN Xiang\|gang;  ZHONG Yi;  JIANG Xue\|liang
School of Materials Science and Engineering, Wuhan Institute of Technology, Wuhan 430074, China
关键词:
高吸水性树脂的制备; 反相悬浮聚合; 吸水倍率
Keywords:
synthesis of superabsorbent resin;  inverse suspension copolymerization;  water absorbent ration
分类号:
TQ322.4
DOI:
:103969/jissn16742869201205001
文献标志码:
A
摘要:
以丙烯酸(AA)、丙烯酰胺(AM)、2\|丙烯酰胺\|2\|甲基丙磺酸(AMPS)和二甲基\|二烯丙基氯化铵(DMDAAC)为单体，采用反向悬浮聚合法，以过硫酸钾(KPS)为引发剂，N，N\|亚甲基双丙烯酰胺为交联剂，Span80为分散剂，在环己烷连续相下进行四元共聚，制备出了耐盐性高吸水树脂.研究了丙烯酸和丙烯酰胺不同配比对吸水率的影响，实验结果表明：当AA∶AM=4∶1时，在蒸馏水、0.9%(质量分数)的NaCl溶液、2%(质量分数)的NaCl溶液、5%(质量分数)的NaCl溶液中的最大吸水量分别为500 g/g、200 g/g、150 g/g、60 g/g.通过与传统三元共聚树脂(AA/AMPS/DMDAAC)的红外分析(FT\|IR)和热重分析(TG)比较，表明几种单体产生了交联，且有较好的协同作用；并对四元共聚产物进行了粒度测试及扫描电镜分析(SEM)，确定了其微观形貌.
Abstract:
The AA\|AM\|AMPS\|DMDAAC four component copolymer of salt\|tolerant superabsorbent resin with high absorbability in saline and high absorption rate was synthesized by inverse suspension copolymerization, with Cyclohexane as dispersing medium, Span\|80 as dispersing agent, K2S2O8 as initator, N,N\|Methylenebisacrylamide as cross\|linking agent. The effects of different mass ratio between acrylic acid and acrylamide on water absorption were studied, and the results show that when the mass ratio is m(AA)∶m(AM)=4∶1, the salt\|resistant superabsorbent resin has the best water absorbing capacity,the swelling capacity of pure water, 0.9% NaCI solution, 2% NaCI solution and 5% NaCl solution is found to be 500 g.g-1, 200 g.g-1, 150 g.g-1 and 60 g.g-1, respectively. Compared to traditional multigroup\|cooperated superabsorbent resin(AA/AMPS/DMDAAC) by Fourier transform infrared spectroscopy (FT\|IR) and Thermogravimetric analysis (TG)，these monomers have linked each other and the function groups have cooperated effectively；microscopic morphology of quaternary product are determined by particle size measurement and scanning electron microscopy (SEM).

参考文献/References:

［1］Lee W,Wu R.Superabsorbent polymeric Materials.1.Swelling behaviors of Crosslinked poly(sodium acrylate-co-hydroxyethyl methacrylate)in Aqueous salt solution［J］.Jonual of Applied Polymer Science,1998,62(7):1099-1114.
［2］陈创前, 蔡会武, 章结兵，等. 互穿网络耐盐性高吸水树脂的制备与表征［J］. 化工新型材料, 2008, 36(8): 108-110.
［3］高锦章, 朱文娟, 李岩，等. 辉光放电电解等离子体引发制备三元共聚耐盐性高吸水树脂［J］.西北师范大学学报, 2010（1）: 70-74.
［4］王月珍, 周柳茵, 邵华德，等. 耐盐性高吸水树脂的制备及其性能研究［J］. 功能材料, 2007, 38(A09): 3375-3377.
［5］葛艳蕊, 张炳烛, 冯薇，等. 耐盐性高吸水树脂的反相悬浮制备过程及其结构表征［J］. 日用化学工业, 2007, 37(1): 20-23,27.
［6］马松梅, 柳明殊，曹丽歆，等. 丙烯酸盐与丙烯酰胺共聚制备耐盐性高吸水树脂［J］. 功能高分子学报, 2003, 16(4): 502-506.
［7］张宇, 叶华, 赵建青，等. 耐盐性高吸水树脂的研究进展［J］. 合成材料老化与应用, 2003, 32(3): 42-47.
［8］默丽敏, 王锡臣, 项爱民. 耐盐性高吸水树脂的合成研究［J］. 现代塑料加工应用, 2000, 12(2): 21-23.
［9］谭德新, 王艳丽, 吉小利，等. 紫外辐射法合成四元共聚高吸水性树脂及其性能研究［J］. 精细石油化工, 2010, 27(5): 65-68.
［10］Flory P J. Principles of polymer chemistry［M］. Amaion：World Publishing Company,2003:672.

相似文献/References:

备注/Memo

备注/Memo:
收稿日期：20120112基金项目：国家自然科学基金项目（507737）；湖北省科技攻关项目（2002AA07B02）作者简介：周爱军(1965-)，男，湖北武汉人，副教授，硕士研究生导师.研究方向：材料加工.
更新日期/Last Update: