[1]李　亮,喻航达,邱唯楚,等.海藻酸钠/氧化石墨烯复合水凝胶的制备与性能[J].武汉工程大学学报,2018,40(06):641-644.[doi:10. 3969/j. issn. 1674?2869. 2018. 06. 011]
　LI Liang,YU Hangda,QIU Weichu,et al.Preparation and Properties of Sodium Alginate/Graphene OxideCompoiste Hydrogels[J].Journal of Wuhan Institute of Technology,2018,40(06):641-644.[doi:10. 3969/j. issn. 1674?2869. 2018. 06. 011]
点击复制

海藻酸钠/氧化石墨烯复合水凝胶的制备与性能(/HTML)
分享到：

《武汉工程大学学报》[ISSN:1674-2869/CN:42-1779/TQ]

卷:
40
期数:
2018年06期
页码:
641-644
栏目:
材料科学与工程
出版日期:
2018-12-28

文章信息/Info

Title:
Preparation and Properties of Sodium Alginate/Graphene OxideCompoiste Hydrogels
文章编号:
20180611
作者:
李　亮; 喻航达; 邱唯楚; 申小松; 喻湘华
武汉工程大学材料科学与工程学院，湖北 武汉 430205
Author(s):
LI Liang; YU Hangda; QIU Weichu; SHEN Xiaosong; YU Xianghua
School of Materials Science and Engineering，Wuhan Institute of Technology， Wuhan 430205， China
关键词:
海藻酸钠; 氧化石墨烯; 复合水凝胶
Keywords:
sodium alginate;  graphene oxide;  composite hydrogel
分类号:
O633
DOI:
10. 3969/j. issn. 1674?2869. 2018. 06. 011
文献标志码:
A
摘要:
为了研究氧化石墨烯（GO）对海藻酸钠（SA）凝胶性能的影响，以Ca2+与Fe3+作为交联剂，在SA水凝胶自组装过程中加入GO水溶液，一步法得到了海藻酸钠/氧化石墨烯（SA/GO）复合水凝胶。通过扫描电子显微镜与X射线衍射表征了所得凝胶的结构与微观形貌，测试了不同凝胶样品的平衡溶胀性能和力学性能。研究结果表明，Fe3+交联得到的凝胶结构相比Ca2+交联得到的凝胶更加紧凑，平衡溶胀性能降低较多；随着GO的加入，复合水凝胶的力学性能提升，平衡溶胀性能降低，这表明SA/GO复合水凝胶的性能可以通过选择合适的交联剂与GO用量进行调控。关键词：海藻酸钠；氧化石墨烯；复合水凝胶
Abstract:
To study the effect of graphene oxide（GO） on the property of sodium alginate（SA） hydrogel，the sodium alginate/graphene oxide（SA/GO） composite hydrogel was prepared through the addition of GO in the self-assembly process of SA hydrogel using Ca2+ or Fe3+ as crosslinking agents. The morphology and structure of the as-prepared hydrogels were characterized by scanning electron microscopy and X-ray diffraction， and their equilibrium swelling degree and mechanical strength were also measured. The experimental results show that the equilibrium swelling degree of the hydrogel crosslinked by Fe3+ is significantly decreased with more compacted microstructure，compared with that of the hydrogel crosslinked by Ca2+. The mechanical strength of the composite hydrogel improves and the equilibrium swelling degree decreases with the increase of GO，indicating that the property of SA/GO composite hydrogel can be controlled with crosslinking agent and amount of GO.

参考文献/References:

［1］　VOORHAAR L，HOOGENBOOM R. Supramolecular polymer networks：hydrogels and bulk materials［J］. Chemical Society Reviews，2016，45（14）：4013-4031. ［2］　AHMED E. Hydrogel：preparation，characterization，and applications：a review［J］. Journal of Advanced Research，2015，6（2）：105-121. ［3］　武泽林，熊惠之，喻湘华，等. 聚苯胺-多糖复合凝胶的制备及其染料吸附性能［J］. 武汉工程大学学报，2017，39（4）：348-352. ［4］　HERBER S， OLTHUIS W. Exploitation of a pH- sensitive hydrogel for CO2 detection ［J］. Sensors & Actuators B Chemical，2017，103（1）：284-289. ［5］　ZRID R，BENTISS F，ATTOUMANE BEN ALI R，et al. Potential uses of the brown seaweed cystoseira humilis biomass：1-sodium alginate yield，FT-IR，1H NMR and rheological analyses ［J］. Journal of Materials & Environmental Science，2016，7（2）：613-620. ［6］VARAPRASAD K，RAGHAVENDRA G M，JAYARAMUDU T，et al. Nano zinc oxide-sodium alginate antibacterial cellulose fibres ［J］. Carbohydrate Polymers，2016，135：349-355. ［7］　THAKUR S，PANDET S，AROTIBA O A. Development of a sodium alginate-based organic/inorganic superabsorbent composite hydrogel for adsorption of methylene blue ［J］. Carbohydrate Polymers，2016，153：34-46. ［8］　JABEEN S，CHAT O A，MASWAL M，et al. Hydrogels of sodium alginate in cationic surfactants：surfactant dependent modulation of encapsulation/release toward Ibuprofen ［J］. Carbohydrate Polymers，2015，133：144-153. ［9］　LI J，JIANG C Q，LANG X Q，et al. Multilayer sodium alginate beads with porous core containing chitosan based nanoparticles for oral delivery of anticancer drug ［J］. International Journal of Biological Macromolecules，2016，85：1-8. ［10］　LI X L，QI Y X，LI Y F，et al. Novel magnetic beads based on sodium alginate gel crosslinked by zirconium（IV） and their effective removal for Pb2+ in aqueous solutions by using a batch and continuous systems ［J］. Bioresource Technology，2013，142（4）：611-619. ［11］　KAMATA H，AKAGI Y，KAYASUGA-KARIYA Y， et al. "Nonswellable" hydrogel without mechanical hysteresis ［J］. Science，2014，343（6173）：873-875. ［12］　GEIM A K. Graphene：status and prospects ［J］. Science，2009，324（5934）：1530-1534. ［13］　赵睿，汪洋，柳景亚，等. 四氧化三锰/聚吡咯/石墨烯复合材料的研制［J］. 武汉工程大学学报，2015，37（8）：45-48. ［14］　TRANG L K H， TUNG T T， YOUNG K T， et al. Preparation and characterization of graphene composites with conducting polymers ［J］. Polymer International，2012，61（1）：93-98. ［15］　PARK S，DIKIN D A，NGUYEN S B T，et al. Graphene oxide sheets chemically cross-linked by polyallylamine ［J］. Journal of Physical Chemistry C，2009，113（36）：15801-15804. ［16］　XU Y，WU Q，SUN Y，et al. Three-dimensional self- assembly of graphene oxide and DNA into multifunctional hydrogels ［J］. ACS Nano，2010，4（12）： 7358-7362. ［17］　朱珍妮，熊惠之，喻湘华，等. 氮掺杂石墨烯/聚苯胺复合凝胶的制备与性能［J］. 武汉工程大学学报，2016，39（5）：455-460.

相似文献/References:

[1]张桥,鄢国平,程巳雪.点击化学反应原位制备海藻酸钠水凝胶[J].武汉工程大学学报,2011,(07):14.
　ZHANG Qiao,YAN Guoping,CHENG Sixue.Preparation of alginate hydrogels via “click” chemistry[J].Journal of Wuhan Institute of Technology,2011,(06):14.
[2]伍甜甜,赵　睿,陈宇欣,等.海藻酸钠海绵的制备及其药物控释性能[J].武汉工程大学学报,2018,40(05):534.[doi:10. 3969/j. issn. 1674-2869. 2018. 05. 011]
　WU Tiantian,ZHAO Rui,CHEN Yuxin,et al.Preparation and Controlled Release Performance of Sodium Alginate Sponges as Drug Carrier[J].Journal of Wuhan Institute of Technology,2018,40(06):534.[doi:10. 3969/j. issn. 1674-2869. 2018. 05. 011]
[3]张　欢,王　飞,陈珠玉,等.银纳米线复合柔性透明电极的制备与表征[J].武汉工程大学学报,2021,43(03):294.[doi:10.19843/j.cnki.CN42-1779/TQ.202008022]
　ZHANG Huan,WANG Fei,CHEN Zhuyu,et al.Preparation and Characteristics of Composite Flexible Transparent Electrodes of Silver Nanowires[J].Journal of Wuhan Institute of Technology,2021,43(06):294.[doi:10.19843/j.cnki.CN42-1779/TQ.202008022]

备注/Memo

备注/Memo:
收稿日期：2018-03-06基金项目：武汉工程大学第九届研究生教育创新基金（CX2017001）；2017年地方高校国家级大学生创新创业训练计划项目（201710490004）作者简介：李　亮，博士，教授。 E-mail：[email protected]引文格式：李亮，喻航达，邱唯楚，等. 海藻酸钠/氧化石墨烯复合水凝胶的制备与性能［J］. 武汉工程大学学报，2018，40（6）：641-644.
更新日期/Last Update: 2018-12-22