Title:
Synthesis of waterbased acrylic emulsion
文章编号:
16742869(2013)04003005
作者:
官仕龙; 陈协; 胡登华; 陈思
武汉工程大学绿色化工过程教育部重点实验室，湖北省新型反应器与绿色化学工艺重点实验室，湖北 武汉 430074
Author(s):
GUAN Shilong; CHEN Xie ;  HU Denghua; CHEN Si
Key Laboratory for Green Chemical Process of Ministry of Education, Hubei Key Laboratory of Novel Reactor and Green Chemical Technology,School of Chemical Engineering and Pharmacy, Wuhan Institute of Technology, Wuhan 430074, China
关键词:
丙烯酸树脂; 水性; 乳液聚合; 过硫酸铵
Keywords:
acrylic resin;  waterborne;  emulsion polymerization;  ammonium persulfate
分类号:
TQ433.436
DOI:
103969/jissn16742869201304007
文献标志码:
A
摘要:
以甲基丙烯酸为功能性单体、苯乙烯为硬单体和丙烯酸正丁酯为软单体，通过3种基本丙烯酸酯类单体用乳液聚合的方法合成了一种水性丙烯酸乳液.甲基丙烯酸作为功能单体实现水溶性并增加了附着力.研究了单体配比、引发剂种类及用量、反应温度、搅拌速度、单体滴加时间和保温时间对乳液及涂膜性能的影响.实验结果表明，单体甲基丙烯酸、苯乙烯和丙烯酸正丁酯的质量配比为5∶17∶20，单体混合物的的滴加时间为2~3 h, 引发剂过硫酸铵其用量为单体质量的0.7%，加入方式为与单体同时逐滴加入，乳化剂选用OP10和十二烷基硫酸钠的复合乳化剂，其用量分别为单体质量的2%和1%, 反应温度为75~85 ℃，搅拌速度为200~300 r/min，可以制得到稳定性很好的白色带蓝光的乳液，100 ℃下烘干可得到硬度、附着力和柔韧性都很好的无色透明涂膜
Abstract:
An aqueous acrylic emulsion was synthesized by the method of emulsion polymerization with methacrylate as a functional monomer, styrene as a hard monomer and nbutyl acrylate as a soft monomer. The methacrylic acid as the functional monomer achieved watersoluble and increased the adhesion. The effects of the monomer ratio, kind and amount of initiator agent, reaction temperature, stirring speed , monomer dropping time and the holding time on the emulsion and film properties were discussed. The experimental results show that the mass proportion of methacrylate, styrene and nbutyl acrylate is 5∶17∶20, the dropping time of the monomer mixture is from 2 to 3 h, the use amount of initiator ammonium persulfate is 0.7% of the monomer mass, adding dropwise simultaneously with the monomer, OP10 and sodium lauryl sulfate were selected as the emulsifier content with 2% and 1% of the monomer mass respectively, the reaction temperature is from 75 ℃ to 85 ℃ and the stirring speed is from 200 to 300 r/min, white emulsion with obviously blue light and good stability is obtained; under 100 ℃, colourless and transparent film with good hardness, adhesion and flexibility is obtained.

参考文献/References:

［1］吴跃焕．木器涂料用高固含量苯乙烯一丙烯酸酷微乳液的合成及机理研究\[D\]．广州：华南理工大学，2003:8．［2］涂伟萍．水性涂料\[M\].北京:化学工业出版社，2006:216．［3］赵全生.我国丙烯酸树脂漆的进展\[J\]．中国涂料，1996(6)：515．［4］潘祖仁．高分子化学\[M\]．北京：化学工业出版社，1995．［5］Atik S S，Thomas J K ．Photochemistry　in polymerized MicrOemulSionSystem\[J\]．J Am Chem Soc,1982，104：58685876．［6］钟强锋．水性丙烯酸树脂的合成及其改性的研究\[D\]．广州：广东工业大学，2007:5．［7］张光霞，韩雪峰，田华．聚丙烯酸酯乳液的制备及其性能测定\[J\]．研发前沿，2009，17（20）：1819．［8］苗小，孙道兴，于健．外交联功能型丙烯酸乳液涂料的制备\[J\]．化学与黏合,2011,33(1)：58．［9］吴胜华, 姚伯龙,陈明清,等．功能型丙烯酸乳液的合成及其性能\[J\]．江南大学学报,2003,2(3)：293296．

相似文献/References:

[1]王天晴,傅光华,陶　齐,等.功能性丙烯酸树脂的制备与应用[J].武汉工程大学学报,2019,(06):522.[doi:10. 3969/j. issn. 1674-2869. 2019. 06. 003]
　WANG Tianqing,FU Guanghua,TAO Qi,et al.Preparation and Application of Functional Acrylic Resin[J].Journal of Wuhan Institute of Technology,2019,(04):522.[doi:10. 3969/j. issn. 1674-2869. 2019. 06. 003]
[2]刘茂松,张松鹏,程 凯,等.光固化丙烯酸阴极电泳涂料的制备及性能研究[J].武汉工程大学学报,2023,45(02):0.[doi:10.19843/j.cnki.CN42-1779/TQ.202301007]
　LIU Maosong,ZHANG Songpeng,CHENG Kai,et al.Preparation and Properties of Photo-Curing Acrylic Acid CathodeElectrocoatings[J].Journal of Wuhan Institute of Technology,2023,45(04):0.[doi:10.19843/j.cnki.CN42-1779/TQ.202301007]

备注/Memo

备注/Memo:
作者简介：官仕龙(1963)，男，江西临川人，教授，硕士研究生导师.研究方向: 环保型涂料、精细化工产品、助剂、医药和农药中间体、功能高分子材料.第35卷第4期2013年04月武汉工程大学学报JWuhanInstTechVol35No4Apr.2013
更新日期/Last Update: 2013-05-18